Prestressing in wood connection, due to frictional forces, improves mechanical properties of the connection. This paper presents novel friction-based connectors, and corresponding tests at the connection and system levels. The friction-base connector is composed of a softwood or hardwood dowels inserted into the wood-based material and tightened to generate frictional force. Long-term performance was evaluated by stress relaxation tests and time-dependent connection tests. To evaluate dynamic performance of shear walls with friction-based connectors, shake table tests were conducted. The shake table tests showed that the restoring force characteristics of the wood friction shear walls were bilinear reflecting the behaviors of the friction-based connectors. The strength degradation of the wood friction shear walls due to cyclic input was small that more seismic inputs could be applied before any significant damage to the wood friction shear wall. Results of stress relaxation tests, for periods of 1 to 3 years, showed that the stresses were maintained at 70–90% under uncontrolled environment. On the other hand, the results of time-dependent connection tests, for 1 to 6 years, showed high initial clamping stresses caused large performance loss, but high performance could be maintained when tightened below the allowable stress for sustained loading.

<title>Abstract</title>In this study, the columns with interior notches in traditional Japanese timber frames were selected as the research object, and static bending tests were performed to investigate the effect of interior notches on the flexural properties of columns. First, the bending behaviors of columns under three-point and four-point load configurations were compared to obtain a suitable referenced strength of a column without notches. The reduction in the load-bearing capacity of columns with different types of interior notches in traditional Japanese timber structures was determined through experimental tests and statistical analysis. The results indicated that the mean bending strength of columns with three different notch types was consistent with those without notches, the continuous timber on both sides of the notch had a beneficial effect on maintaining a higher strength and reducing the stress intensity around the notch. The fracture position and the standard deviation of the bending strength were affected not only by the notch depth, but also by the notch width on the tensile side of the column.